CRMO po'lat qotishmasi po'lat quvurining odatiy kimyoviy tarkibi nima?
CRMO po'lat o'g'lisi po'lat quvurning asosiy qismlari - bu xrom (CR) va Oddiy baholar 15% {{} {{}}. 18% {{}}. 18% {{cr) 0. 8 0% -1% -1 {{MO) 0,60% {{mn), marganrans (P), oltingugurt (p) dan (p)). Chromium qo'shilishi po'latning oksidlanishiga qarshilik va korroziya qarshiligini yaxshilaydi, molibden esa yuqori haroratli va krepni kuchaytiradi. Ushbu ingredientlarning bu kombinatsiyasi kran va yuqori harorat va yuqori bosimli muhitga, masalan, elektr stantsiyalari va neft-kimyo uskunalari kabi krandagi po'lat po'chaminadi.
CRMO po'lat qotishmaining mexanik xususiyatlari qanday?
CRMO PRELLOY QANDAY QINGI MA'LUMOT QISMLARI Mexanik xususiyatlarga ega. Odatda 15cro ning keskinlik kuchi odatda 440-640 295mpa dan katta yoki tengdir va uzilish 19% dan katta yoki unga teng. Valdium (V) ning mavjudligi sababli 12cr1mov yuqori haroratli kuchga ega va hali ham 550 darajaga yuqori tirnash xususiyati olib borishi mumkin. CRMO po'latining qattiqligi odatda HB {{}} - bu yanada yaxshilanib, uni chayqab, yanada yaxshilanishi mumkin. Oddiy uglerod po'lat bilan taqqoslaganda, CRMO po'latlari yuqori haroratda sekinroq kuchga ega, shuning uchun u termal quvurlar va bosimli tomirlarda keng qo'llaniladi.
CRMO po'lat qotishmasi po'lat quvurining yuqori haroratga chidamliligi nima?
CrMo steel alloy steel pipe performs well in high temperature environments. 15CrMo can be used for a long time below 500℃, and 12Cr1MoV is suitable for high temperature conditions below 580℃. The dense oxide film (Cr₂O₃) formed by chromium can effectively prevent further oxidation, while molybdenum improves the creep resistance of steel. In power plant boilers, CrMo steel pipes are often used in superheaters and reheaters, and can withstand the erosion of high-temperature and high-pressure steam. Compared with austenitic stainless steel, CrMo steel has a lower cost, but higher-grade alloy steels are still required in extremely high-temperature (>600 daraja) muhit.
CRMO po'lat qotishmalarining payvandlash faoliyati qanday?
CrMo steel alloy steel pipes have good welding performance, but due to their high alloy content, preheating (200-300 degree ) and post-weld heat treatment (600-650 degree annealing) are required during welding to prevent cold cracks and hydrogen embrittlement. Oradan foydalanilgan payvandlash usullari arc arc payvandlash (R307 elektrodidan foydalangan holda), yassi payvandlash va TIG payvandlash materiallarini o'z ichiga oladi. Payvandlash stressini kamaytirish uchun intervalli devorli quvurlar bilan shug'ullanish kerak va ko'p peshqadamlik payvandlanishi kerak. Noto'g'ri bo'lmagan sinov (masalan, UT, RT) payvand choki sifatini ta'minlash uchun payvandlash kerak.
CRMO po'lat qotishmalari uchun issiqlikni davolash jarayoni qanday?
CRMO po'latdan yasalgan pashshalarining issiqlikni tozalash jarayoni asosan normallashtirish, muloyim va qonni o'z ichiga oladi. Normallashtirish (900-930}}} darajani) donalarni tozalab, kuch va qattiqlikni yaxshilashi mumkin; Imtiyoz (600-680} darajasi ichki stressni yo'q qilish va plastikni yaxshilash uchun ishlatiladi; Qalinish va tebranish (yuqori haroratni yumshatish) eng yaxshi mexanik xususiyatlarga ega bo'lishi mumkin. Hukuster naychalari uchun, normallashtirish + tozanatlash jarayonida odatda haroratning yuqori darajada yuqori talablariga javob berish uchun ishlatiladi. Issiqlikni davolashdan keyin CRM po'latida, shuningdek, tuzilishning bir xilligini ta'minlash uchun qattiqlik sinovlari va metalografik tahlilga muhtoj.